Density 1.80g 1.85g/cm3 Graphite Round Rod Vibration Forming Way for Customized Needs
Product Details:
| Place of Origin: | China |
Payment & Shipping Terms:
| Minimum Order Quantity: | 1 Piece |
|---|---|
| Delivery Time: | Peak Season Lead Time: 6-12 months, Off Season Lead Time: 1-3 months |
| Payment Terms: | LC, T/T, D/P, PayPal, Western Union, Small-amount payment, Money Gram |
|
Detail Information |
|||
| Model NO.: | DC-1.80 | Grade: | Industrial Grade |
|---|---|---|---|
| Crystal Morphology: | Flake Graphite | Composition: | 100% Carbon |
| Forming Way: | Vibration | Transport Package: | By Ply-Wood |
| Specification: | Customized | Trademark: | DC |
| Origin: | Beijing, China | HS Code: | 2701110090 |
| Supply Ability: | 100PCS Each Day | Customization: | Available |
| Carbon Content: | High-Carbon | Bulk Density: | 1.6 |
Product Description
density 1.80g 1.85g/cm3 graphite round rod:
On the following is the density:1.72g/cm3, grain size:0.8mm
Molded graphite are mainly used to machine graphite molds and other machined graphite parts with higher requirements. 1-used as graphite molds in fields such as glass, non-ferrous, rare earth, precious metal, or graphite mold, crucible and other machine graphite parts in automobile industries. 2-used as EDM graphite electrode and mold.3-used as structural material or parts of high temperature furnace.
Contact Informations:
| Grade | bulk density | compressive strength | bending strength | electric resistivity | Ash content |
| 180 | 1.80g/cm3 | 65MPA | 38mpa | 8-11 | 50PPM |
| 185 | 1.85g/cm3 | 85 mpa | 46 mpa | 8-10 | 50PPM |
On the following is the density:1.72g/cm3, grain size:0.8mm
| Sizes of block | unit weight (KG) | bulk density | compressive strength | bending strength | electric resistivity | ash content |
| 740*400*2300mm 740*360*2300mm 650*400*2000mm 650*360*2000mm 500*500*1950mm 500*400*1900mm 400*400*2200mm | 1368 1191 1037 907 929 795 752 | 1.72g/cm3 | >48MPA | >23 MPA | <8 | <0.15 |